Novel Quaternary Ammonium Urethane-Dimethacrylates for Copolymers with Low Water Sorption and Solubility

Six novel urethane-dimethacrylates with quaternary ammonium groups (QAUDMAs) were successfully synthesized from 2-(methacryloyloxy)ethyl-2-hydroxyethylmethylalkylammonium bromide (QAHAMA-n, where n was 8 and 10) and diisocyanate (isophorone diisocyanate (IPDI), 4,4′-methylenedicyclohexyl diisocyanate (CHMDI), and 4,4′-diphenylmethane diisocyanate (MDI)). Their chemical structures were confirmed through nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FTIR). The refractive index (RI) and density (d_m) were also determined. The novel QAUDMAs were compounded with common dental dimethacrylates and subsequently photopolymerized. The resulting copolymers, comprising QAUDMA 40 wt.%, bisphenol A glycerolate dimethacrylate (Bis-GMA) 40 wt.%, and triethylene glycol dimethacrylate (TEGDMA) 20 wt.%, were tested for water sorption (WS) and solubility (SL). The WS and SL values decreased following these orderings based on the diisocyanate: IPDI > CHMDI > MDI for WS, and MDI > CHMDI > IPDI for SL. The WS values ranged from 11.50 to 13.82 µg/mm³, and were significantly lower than the recommended maximum for dental materials, 40 µg/mm³. The SL values that met the recommended maximum, 7.5 µg/mm³, ranged from 2.67 to 6.75 µg/mm³. Only the copolymer having the QAHAMA-8- and MDI-derived QAUDMA had the SL slightly exceeding 7.5 µg/mm³, at 7.89 µg/mm³.