The Effect of Irradiation Dose and Temperature on Irradiation Hardening and Microstructure Study of Hot-Forged V-4Cr-4Ti Under Self-Ion Irradiation

Yaxia Wei Yinshu Zhao Min Xu Pengfei Zheng Liping Guo +4 lainnya

Abstrak

After being self-ion implanted at 400 °C and 550 °C, the microstructure and irradiation hardness of kilogram-scale V-4Cr-4Ti alloys were studied using a transmission electron microscope (TEM) and nano-indentation test technology. Irradiation was performed using self-ions (V2+) at 2.5 MeV with design influences of 1.15 × 1015 ions cm−2, 4.59 × 1015 ions cm−2, and 9.17 × 1015 ions cm−2, so that the peak damages of V-4Cr-4Ti alloys are 1, 4, and 8 dpa, respectively. Compared with the 400 °C samples, the 550 °C samples exhibited a higher-density number of dislocation loops and increased hardness and reached saturation at lower irradiation doses. The irradiation temperature was mainly responsible for these differences, and the potential mechanism for its effect on the irradiation behavior was discussed.

Topik & Kata Kunci

Mining engineering. Metallurgy

Penulis (9)

Yaxia Wei

Yinshu Zhao

Min Xu

Pengfei Zheng

Liping Guo

Hongtai Luo

Pengbo Zhang

Guihang Zhang

Hua Zhao

Format Sitasi

APA MLA BibTeX

Wei, Y., Zhao, Y., Xu, M., Zheng, P., Guo, L., Luo, H. et al. (2025). The Effect of Irradiation Dose and Temperature on Irradiation Hardening and Microstructure Study of Hot-Forged V-4Cr-4Ti Under Self-Ion Irradiation. https://doi.org/10.3390/met15020104

Akses Cepat

PDF tidak tersedia langsung

Cek di sumber asli →

Lihat di Sumber doi.org/10.3390/met15020104

Informasi Jurnal

Tahun Terbit: 2025
Sumber Database: DOAJ
DOI: 10.3390/met15020104
Akses: Open Access ✓