Effect of Al/Cu Ratio on Microstructure and High-Temperature Oxidation Resistance of Al_xCoCrCu_yFeNi High-Entropy Alloy Coatings

To improve high-temperature oxidation resistance for Ti6Al4V alloy, Al_xCoCrCu_yFeNi (x = 0, 0.3, 0.5, 0.7, 1.0; y = 1.0, 0.7, 0.5, 0.3, 0, x + y = 1.0) high-entropy alloy (HEA) coatings were prepared on the Ti6Al4V alloy substrate by a laser cladding technique. The results show that the coatings were mainly composed of FCC, BCC, and Ti-rich phases. Severe segregation of the Cu element occurred in the CoCrCuFeNi HEA coatings as a Cu-rich phase (FCC2). The Cu-rich phases decreased with a decreasing Cu content and completely disappeared until the Al content reached 1.0. The microhardnesses of the Cu_1.0, Cu_0.7Al_0.3, Cu_0.5Al_0.5, Cu_0.3Al_0.7, and Al_1.0 HEA coatings were 2.01, 2.06, 2.08, 2.09, and 2.11 times that of the substrate, and compared with those of a Ti6Al4V alloy substrate, the oxidation rates of the HEA coatings decreased by 55%, 51%, 47%, 42%, and 35%, respectively. The surface oxides of the five coatings were mainly composed of CuO, TiO₂, Fe₃O₄, Cr₂O₃, and Al₂O₃. The increase in the Al content promoted the generation of Al₂O₃ film and Cr₂O₃ on the surfaces of the coatings, which significantly improved the high-temperature antioxidant performance of the high-entropy alloy coatings for 50 h at 800 °C. When x = 1.0, the coating showed the best high-temperature antioxidant performance.