Microstructure, Friction and Wear Behavior and Corrosion Resistance of electroless Double-Layer Ni-P/Ni-Mo-P Coatings on AZ91D Magnesium Alloy
Abstrak
Double-layer Ni-P coatings with low phosphorus content in the inner layer and high phosphorus content in the outer layer and Ni-Mo-P composite coatings are successfully prepared on the surface of AZ91D magnesium alloy by chemical plating process. The microstructures, friction and corrosion resistance of double-layer Ni-P and Ni-Mo-P coatings are studied in comparison. Meanwhile, the deposition and corrosion resistance mechanism for the coatings are investigated. Results convey that both Ni-P and Ni-Mo-P coatings showcase an amorphous structure. The coating possesses denser and more homogeneous structure with the co-doping of Mo. The micro-indentation hardness (859.7 HV) and friction coefficient (0.58) of Ni-Mo-P coatings show that the ternary alloy coating is firmly bonded to the magnesium alloy substrate. Besides, the Ni-Mo-P coatings demonstrate exceptional wear resistance attributed to Mo co-deposition, fostering grain refinement and facilitating the growth of passivation films.
Topik & Kata Kunci
Penulis (10)
Jingpei Liu
Wanchang Sun
Eryong Liu
Xiaojia Liu
Congxiao Zhang
Yifan Xu
Mengran Zhou
Bo Zhang
Hui Cai
Jingli Zhang
Akses Cepat
PDF tidak tersedia langsung
Cek di sumber asli →- Tahun Terbit
- 2024
- Sumber Database
- DOAJ
- DOI
- 10.1590/1980-5373-mr-2023-0379
- Akses
- Open Access ✓