Preparation and electromagnetic absorbing properties of TiC/Ni powders

ZHANG Sen LIU Yi SU Xiaolei LI Yunyu YIN Yiqiu

Abstrak

In order to improve the microwave absorption performance of TiC powder, TiC/Ni composite powder was prepared by coating nickel particles with mass fraction of 10%, 20% and 30% on the surface of TiC by typical coarsening and sensitizing electroless nickel plating process. The composite powder was characterized by SEM and XRD, and the effect of nickel content on the microwave absorbing properties of TiC/Ni composite powder was analyzed. The results shows that the dielectric constant and permeability of TiC/Ni powder increases with the increase of nickel mass fraction. With -5 dB as the scale, the absorption bandwidth of the sample with a thickness of 3.0 mm increases from 0 to 3.34 GHz. When the thickness is 3.8 mm, the minimum reflection loss of TiC is -3.66 dB. For TiC/Ni samples with a thickness of 2.8 mm and a mass fraction of Ni of 30%, the minimum reflection loss value of -9.95 dB is obtained at 9.67 GHz. It can be seen that electroless nickel plating can improve the microwave absorption performance of TiC.

Topik & Kata Kunci

Materials of engineering and construction. Mechanics of materials Environmental engineering

Penulis (5)

ZHANG Sen

LIU Yi

SU Xiaolei

LI Yunyu

YIN Yiqiu

Format Sitasi

APA MLA BibTeX

Sen, Z., Yi, L., Xiaolei, S., Yunyu, L., Yiqiu, Y. (2022). Preparation and electromagnetic absorbing properties of TiC/Ni powders. https://doi.org/10.13338/j.issn.1674-649x.2022.01.005

Akses Cepat

PDF tidak tersedia langsung

Cek di sumber asli →

Lihat di Sumber doi.org/10.13338/j.issn.1674-649x.2022.01.005

Informasi Jurnal

Tahun Terbit: 2022
Sumber Database: DOAJ
DOI: 10.13338/j.issn.1674-649x.2022.01.005
Akses: Open Access ✓